Amardeep Steel offers HAYNES 188 Sheets, a cobalt-nickel-chromium-tungsten alloy that
is highly suitable for aerospace and commercial gas turbine engine applications. It is commonly used
in the fabrication of combustion cans, flame holders, liners, transition ducts, and afterburner
parts. HAYNES 188 Coils are typically found in the hot sections of engines, specifically in burner
cans, ducting, and afterburner components. However, in recent years, Alloy 230 has gained preference
over Udimet 188 Coils in many applications due to its improved properties.
Udimet 188 Plates possess good forming characteristics and can be forged, hot-worked, or
cold-worked. However, it tends to harden rapidly, necessitating frequent intermediate annealing
treatments for complex forming operations. If you are looking to purchase Alloy 188 Plates, Amardeep
Steel offers them at a reasonable price.
For more information or to inquire about purchasing HAYNES 188 Sheets and Udimet 188 Plates, please
contact Amardeep Steel.
| Specifications | AMS 5608 / AMS 5609 |
| Standard | AMS, AMS and API |
| Specialize | Shim Sheet, Perforated Sheet, B. Q. Profile. |
| Size | 0.5 MM TO 200 MM THICK IN 1000 MM TO 2500 MM WIDTH & 2500 MM TO 12500 MM LENGTH |
| Form | Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) |
| Finish | Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated) |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc. |
| Grade | Haynes 188 (UNS R30188) |
| Chemical Composition Limits | ||||||||||||
| Weight % | C | Mn | Si | P | S | Cr | Ni | W | La | B | Fe | Co |
| Alloy 188 | 0.05-0.15 | 1.25 max | 0.20-0.50 | 0.02 max | 0.015 max | 20-24 | 20-24 | 13-16 | 0.02-0.12 | 0.015 | 3 max | Bal |
| Material | Temp°F | Yield Strength (0.2% Offset) min | Tensile Strength min | Elongation (%) | Hardness | ||
| ksi | MPa | ksi | MPa | ||||
| Alloy 188 Extruded Bar Solution Treated (AMS 5772) |
RT | 55 | 379 | 125 | 862 | 45 |
≤302HB |
| Material | Temp°F | Thickness (Inches) |
Yield Strength (0.2% Offset) min | Tensile Strength min | Elongation (%) | Hardness HRC | ||
| ksi | MPa | ksi | MPa | |||||
| Alloy 188 Sheet Solution Treated (AMS 5608) |
RT | ≤0.020" | 55 | 379 | 125 | 862 | 40 | - |
| Alloy 188 Sheet Solution Treated (AMS 5608) |
RT |
≥0.020" |
55 | 379 | 125 | 862 | 45 | - |
| Alloy 188 Sheet Solution Treated (AMS 5608) |
1200 | ≤0.020" | 36 | 248 | 90 | 621 | 40 | - |
| Alloy 188 Sheet Solution Treated (AMS 5608) |
1200 | ≥0.020" | 36 | 248 | 90 | 621 | 50 | - |
| Haynes 188 Plates | Haynes 188 Plates |
| 188 Haynes Alloy Plates | Haynes 188 Plate |
| Haynes 188 Plate | Haynes UNS R30188 Bright plate |
| Haynes 188 Structural Steel Plates | Prime Haynes 188 Alloy Steel Plate manufacturer |
| Haynes Alloy 188 Cold Rolled Sheet | Corrosion Resistance Super Alloy Haynes 188 Plate |
| UNS R30188 Haynes Alloy Sheets | AMS 5772 Haynes 188 Sheets |
| AMS 5608 Haynes 188 Sheet | Haynes 188 Sheets Stockist |
| High quality 188 Haynes Alloy Plate | Haynes 188 Plates Suppliers |
| Haynes Alloy 188 Plates Dealer | 188 Haynes 5608 Plates Exporter |
| Haynes 188 Plates Stockholder | Haynes Alloy 5772 Plates Distributor |